• Wuxi ShiLong Steel Co.,Ltd.
    John Fairbank
    stainless steel strip with good quality and the Sales clerk service is very good.i like this company i hope can work with your again
  • Wuxi ShiLong Steel Co.,Ltd.
    Fierce Urchin
    good ,the galvanized steel coil quality is good and i donot see the broken on them.that is nice
  • Wuxi ShiLong Steel Co.,Ltd.
    Fleuriau
    Shipment speed is very fast, and the requirements can meet me. Salesman is very responsible.
Contact Person : Miss Jo
Phone Number : 0086 18706170710
WhatsApp : +8618706170710

UNS G51500 AISI 5150 3mm 6mm Aluminium Alloy Sheet Hot Dipped

Place of Origin CHINA
Brand Name OEM/ODM
Certification ISO
Model Number Alloy Steel Plates
Minimum Order Quantity 1 ton
Price negotiable based on the quantity
Packaging Details Standard seaport packing or as custom request
Delivery Time 10-30 days
Payment Terms T/T, Western Union, L/C
Supply Ability 6000 tons per month
Product Details
Standard AISI, ASTM, BS, DIN, GB, JIS Length 1000-4000mm
Shippping Sea Freight MOQ 1 TON
Surface Black / Peeled / Polishing / Port Shanghai
High Light

UNS G51500 AISI 5150 Alloy Steel Products

,

6mm Aluminium Alloy Sheet Hot Dipped

,

aisi 5150 steel

Leave a Message
Product Description

3mm 6mm Aluminium Alloy Sheet Hot Dipped

 

HEAT TREATMENT

Annealing:The microstructure for this alloy to give optimum machinability is one of course lamellar pearlite to coarse spheroidite. This might be obtained by austenitizing at 1380ºF (750ºC) followed by an iso anneal at 1250ºF (680ºC.)

Normalizing: A nominal normalizing temperature for this alloy is 1600ºF (870ºC.) This treatment is followed by air cooling

Hardening: Austenitize at 1475-1550ºF (800-845) and oil quench for small, intricate sections and water quench for large, simple sections.

Tempering: from 1000-1250ºF(540-680ºC) as per required properties.

Machinability: This alloy is readily machined from a coarse pearlite to a coarse spheroidite microstructure.

Weldability: The alloy may be welded but must be preheated and if possible the preheat should be maintained during welding. Welding should be carried out in the annealed condition, not on hardened and tempered material.

 

  • GENERAL CHARACTERISTICS OF ALLOY STEEL 5150 Alloy 5150 is a medium-carbon, chromium steel with good strength, toughness and hardenability
  • APPLICATIONS This alloy is used in the production of fprged components that are subjected to normal stresses for automotive and general engineering.
  • FORGING This alloy would be forged between 2150 and 1600ºF ( 1175 and 870ºC.) The alloy should be slow cooled after forging or transferred to a furnace around the ‘finishing’ temperature.

AISI 5150 Alloy Steel (UNS G51500)


 

Introduction

Alloy steels contain many types of steels whose compositions are more than the limitations of C, Mo, Cr, Va, Mn, Ni, Si, and B fixed for carbon steels. These steels are more responsive to mechanical and heat treatments than carbon steels.

The following datasheet will provide details about AISI 5150 alloy steel.

 

Chemical Composition

The following table shows the chemical composition of AISI 5150 alloy steel.

Element Content (%)
Iron, Fe 97.29-97.97
Manganese, Mn 0.700-0.900
Chromium, Cr 0.700-0.900
Carbon, C 0.480-0.530
Silicon, Si 0.150-0.300
Sulfur, S ≤ 0.0400
Phosphorous, P ≤ 0.0350

Physical Properties

The physical properties of AISI 5150 alloy steel are outlined in the following table.

Properties Metric Imperial
Density 7.85 g/cm3 0.284 lb/in³

Mechanical Properties

The mechanical properties of annealed AISI 5150 alloy steel are provided in the table below.

Properties Metric Imperial
Tensile strength 675 MPa 97900 psi
Yield strength 360 MPa 52200 psi
Elastic modulus 190-210 GPa 27557-30458 ksi
Bulk modulus (typical for steel) 140 GPa 20300 ksi
Shear modulus (typical for steel) 80 GPa 11600 ksi
Poisson’s ratio 0.27-0.30 0.27-0.30
Izod Impact 26 J 19.2 ft.lb
Hardness, Brinell 197 197
Hardness, Knoop (converted from Brinell hardness) 219 219
Hardness, Rockwell B (converted from Brinell hardness) 92 92
Hardness, Rockwell C (converted from Brinell hardness, value below normal HRC range, for comparison purposes only) 13 13
Hardness, Vickers (converted from Brinell hardness) 207 207
Machinability (annealed and cold drawn, based on 100 machinability for AISI 1212 steel) 60 60

Equivalent materials to AISI 5150 alloy steel are as follows.

AFNOR 42 C 2 AFNOR 45 C 2 DIN 1.7006 ASTM A322 ASTM A331 ASTM A505
SAE J770 ASTM A29 ASTM A322 ASTM A331 ASTM A506 ASTM A519
ASTM A752 SAE J1397 SAE J404 SAE J412    

 

 

1. ASME SAE5150,SAE5150H,SAE5155 Carbon steel, SAE5150 Stock , SAE5150 steel plate, SAE5150 steel plate , SAE5150H adopt standard , SAE5150H Technical delivery condition, SAE5150H Mechanical property , SAE5155 price , SAE5155 Impact degree, SAE5155 impact energy.

 

2. Standard: ASTM SAE5150 Carbon steel, SAE5150H stock , SAE5155 Steel Plate.

 

3. Min order requirement:3 tons or earlier according to the heat treatment requirement.

 

4. Adopt Standard: ASTM Standard Specification is Standard Carbon Steels.

 

5. Heat treatment situation or delivery status: Hot rolled, normalized, Annealing, Polishing..

 

6. Third Party :ABS ,DBV ,BV,GL,CCS,LR,RINA,KR,NK,CE,SGS,IKE,IEI or other quality department.

 

7. Test:Test Chemical Component Analysis, Mechanical properties, Technical properties. Exterior Size inspection .Nondestructive Test .Hydrostatic Test

 