Cold Rolled Stainless Steel Sheet
Seamless SS Pipe
Stainless Steel Coil
Stainless Steel Round Bar
Galvanized Steel Pipe
Galvanized Steel Coils
Galvanized Steel Sheet
PPGI Steel Coils
Steel Tin Plate
Mild Steel Square Tube
Carbon Steel Coils
Carbon Steel Sheets
Wear Resistant Steel Plates
Aluminum Steel Sheet
Copper Steel Pipe
Copper Steel Bar
Copper Sheet Coil
Structural Steel Profiles
John Fairbankstainless steel strip with good quality and the Sales clerk service is very good.i like this company i hope can work with your again
Harish kumarأنا راضٍ جدًا عن هذه الصفقة ، ليس فقط لأنهم يشحنون بسرعة ، ولكن أيضًا جودة البضائع جيدة ، وأتطلع إلى التعاون التالي.
RickyCooperate with a trial order. The service is excellent and the price is very good. Product quality is guaranteed and can stand inspection
3mm Cold Rolled Spring Steel Strip Hardened Spring Steel Strip Flat Polished
Contact me for free samples and coupons.
Wechat: 0086 18588475571
If you have any concern, we provide 24-hour online help.x
|Standard||AISI, ASTM, BS, DIN, GB, JIS||Steel Grade||Q195, Q235, SPCC,65Mn, 40CR, S45C,CK75....|
3mm spring steel strip,
3mm cold rolled spring steel strip,
Cold Rolled Spring Steel Strips
Cold Rolled Hardened Spring Steel Flat Wide Applications Polished Bright
65MN Chemical composition
Equivalent Of 65Mn alloy Spring Steel
Heat treatment Related
- Annealing of 65Mn Spring Steel
At first Slowly heated to 730 ℃ and allow enough times, let the steel to be thoroughly heated, Then cool slowly in the furnace. Then 65Mn tool steel will get MAX 250 HB (Brinell hardness).
- Hardening of 65Mn Spring Steel
At the beginning, 65Mn steels should be heated uniformly to 830-860°C (1526-1580°F) until completely heated through. After about 30 min per 25 mm of ruling section is to be provided and then the steels should be immediately quenched in oil. Tempering of 65Mn Spring Steel
Tempering of 65Mn steels is performed at 540°C, Soak well at the selected temperature and soak for at least one hour per 25mm of total thickness. Hardness values at different temperatures after tempering
The mechanical properties of 65Mn Spring Steels are outlined in the following table.
|Tensile strength||Conditions to yield strength||Elongation||Reduction of area||Hardness (Hot Rolled)||Hardness (Cold Drawn)|
|σb (MPa):≥980||σ0.2 (MPa):≥785||δ 5 (%):≥8||ψ (%):≥30||≤302HB;|
65Mn steel, after heat treatment and cold drawing hardening, high strength, it has a certain toughness and plasticity; In the same surface hardening case, completely and the fatigue limit and alloy spring. But hardenability poor, mainly for the smaller size of the spring, such as regulating speed regulating spring, spring load, general machinery in the round, square spiral spring or pull wire for small mechanical spring.
Regular size and Tolerance
Steel round bar: Diameter Ø 2mm – 3000mm
Steel plate: Thickness 2mm – 3000mm x Width 100mm – 3500mm
Steel Hexagonal bar: Hex 5mm – 105mm
Others 65Mn have not specified size, pls contact our experienced sales team.
Moreover, GB 65Mn Spring Steel round bar and flat sections can be cut to your required sizes. 65Mn Spring Steel ground bar can also be supplied by us, providing a high quality Spring Steel precision ground Spring Steel bar to your required tolerances. And GB 65Mn steel is also available as Ground Flat Stock / Gauge Plate, in standard and nonstandard sizes.